Description
? Negative Resist NR9-6000P is a negative tone, thick photoresist designed for 365 nm
wavelength exposure, using tools such as wafer steppers, scanning projection aligners,
proximity printers contact printers.
? These are advantages of NR9-6000P over other resists: - superior resolution capability - fast photospeed - fast develop time - superior adhesion in plating wet etching applications - temperature resistance of up to 100°C - easy resist removal in Resist Remover RR4, or in acetone - shelf life exceeding 3 years at room temperature storage.
? The formulation processing of NR9-6000P were designed with regard to occupational
environmental safety. The principal solvent in NR9-6000P is cyclohexanone
development of NR9-6000P is accomplished in a basic water solution.
Properties
? Solids content (%) 40-43
? Principal solvent cyclohexanone
? Appearance light yellow liquid
? Coating characteristic very uniform,
striation free
? Film thickness after 150°C hotplate bake for 60 s (nm)
Coating spin speed, 40 s spin (rpm): (nm)
1000 11020-12180
1200 10136-11203
1500 8137-8993
2000 7011-7749
3000 5700-6300
4000 4978-5502
? Sensitivity at 365 nm exposure wavelength (mJ/cm2 for 1 μm thick film) 21
? Guaranteed shelf life at 25°C storage (years) 3
Application of resist by spin coating at ed spin speed for 40 s.
Begin dispensing Edge Bead Remover EBR2 simultaneously onto the top bottom
surfaces of the spinning, coated substrate through nozzles 0.5-1.0 cm the edge of
the substrate as soon as edge bead forms (3-5 s after ceasing resist dispense). Stop
dispensing EBR2 5 seconds prior to completion of spin coating cycle.
150°C hotplate bake for 60 s. (softbake)
Resist exposure in a tool emitting 365 nm wavelength.
100°C hotplate bake for 60 s (post-exposure bake).
Resist development in Resist Developer RD6 by spray or immersion.
Development time for 6 μm thick film, for example, is 50 s.
Resist rinse in deionized water until water resistivity reaches prescribed limit.
Drying of resist.
Removal of resist in Resist Remover RR4 at 110°C or in acetone.
Note: The above procedure refers to substrates, which are good conductors of heat such as
silicon, GaAs etc. Bake times need to be increased by a factor of 3.5 for substrates that are
poor conductors of heat such as glass.
Hling Precautions
Negative Resist NR9-6000P is a flammable liquid. Hle it with care. Keep it away heat,
sparks flames. Use adequate ventilation. It may be harmful if swallowed or touched.
Avoid contact with liquid, vapor or spray mist. Wear chemical goggles, rubber gloves
protective coating.